Detailed Selling Lead Description
The product is composed of high quality mullite and high purity fused corundum as a raw materials with addition of specified binder by shaping at high pressure and sintering at high temperature. With features of high refractoriness under load, compact structure, low porosity and high resistance to corrosion, the product are avaiable for the furnace bottom, ceramic cup bottom lining and combined masonry of tuyere, taphole and slag notch of large-sized blast furnace. 
Main technical specification(WGM-1): 
AL2O3 MIN88% 
Fe2O3 MAX1.0% 
Refractoriness MIN1790C 
Bulk density MIN3.0 
Cold crushing strength MIN120MPa 
Cold modulus of rupture MIN20MPa 
0.2MPa RUL MIN1700C